TS-203 Guankoubao is a composite of polymer emulsifiers, which are then pasted by special pasting technology. Its core advantage is that in the process of drying and curing, network interpenetrating structure will be formed, showing the elasticity and flexibility of rubber, which can adapt to structural cracking and vibration, and always maintain the effect of bonding, sealing and waterproofing.
Product characteristics
It is easy to operate,ready to use, smeared directly, cured at room temperature, and can be used on wet base.
Follow-up operation is simple, follow-up construction on waterproof layer can be directly plastered with cement slurry, sticking bricks, etc.
Strong anti-channeling water, strong bonding, sealing and waterproof, with self-healing function, self-repairing seal.
Scope of application
Sealing treatment for all kinds of root parts such as wall-piercing pipe, nozzle, pile head and equipment. All kinds of cracks, large area of coil laying interface bonding treatment and coil lapping edge sealing treatment.
Usage method
1. Base surface requirements: Base surface is free of oil pollution, dust, and slurry is cleaned up, and the base surface is fully wetted with water.
2. Brushing sealant: 100 mm high on the facade, 150 mm wide beyond the orifice of the pipe and 2 mm thick on the facade.
3. Maintenance: After completion of construction, ventilation should be maintained and water should not be immersed before drying and consolidation.
Performance parameter
Reference Dosage:1.5-2.5kgs/㎡
Initial setting time: ≤2hours
Final setting time: ≤5hours
Construction temperature: +5℃~+35℃
Packaging: 1kg/bucket, 4.5kgs/bucket
Implementation standard: JGT501-2016, specific indicators see technical parameters.
Project | Technical standard | ||||
I | II | ||||
Solid content/% | ≥70 | ||||
Surface dry /h | ≤2.0 | ||||
Actual dry /h | ≤5.0 | ||||
Bond strength/Mpa | Drying base surface with cement mortar | ≥0.5% and 100% destruction | ≥0.7% and 100% destruction | ||
Wet base surface with cement mortar | ≥0.3% and 100% destruction | ≥0.5% and 100% destruction | |||
With Aluminum plate | |||||
With plastic | |||||
With glass | |||||
Synchronized curing bond strength | With cement paste | ≥0.5 | |||
With plastic | |||||
With cement mortar | |||||
Water impermeability(0.3Mpa, 30min) | Impervious | ||||
Self-healing | No seepage | ||||
Low temperature flexibility | -10℃,2h no crack | -20℃ 2h no crack | |||
Heat resistance | 80℃ 5h No flowing, sliding, dripping, no dense bubbles on the surface | ||||
Water resistance | 0.6Mpa no string water | ||||
Thermal aging(70℃*168h) | Water resistance | 0.3Mpa, 30min impervious | |||
Low temperature flexibility | -10℃,2h no crack | -15℃ 2h no crack | |||
Bond strength of cement mortar | ≥0.5 | ≥0.7 | |||