TS-106B Hardcover kitchen and toilet (green) waterproofing coating consists of two component waterproof coatings composed of organic polymer emulsion and inorganic powder. The coating has both high strength and high elasticity of rubber materials and durability of inorganic materials. It is a green product recommended by the Ministry of national construction.
Product characteristics
Good temperature resistance, high strength, especially suitable for waterproofing construction of geothermal system;
Excellent anti-ultraviolet, weathering and aging properties;
It can be directly constructed on wet base surface and can resist slight cracking of base.
Scope of application
It is suitable for water-proof and moisture-proof of floor heating system, toilet, kitchen, bathroom, floor, balcony, basement, drinking pool and non-exposed roof.
Usage method
1. Base treatment: The base should have a solid surface structure with porous, rough, crackless, clear water and no empty drum, and the uneven base should be leveled first.
2. Preparation: first, the B component (emulsion) is poured into a clean container, then the A component (powder) is poured into the emulsion, and the electric mixer is used to stir until uniform without caking. Let the slurry rest for 2 to 4 minutes before stirring again.
3. Construction: Brush or spatula is used to coat at least two layers by cross-over method. The first layer is coated with thick coating so that there is no void at all on the base surface. When the first coat has solidified and produced enough strength, about 2 to 4 hours later, the next coat can be constructed. The total coating thickness should be at least 1.0 mm or more. If necessary, the third floor construction can be carried out.
be
Performance parameter
Reference Dosage:1.5-2.0kgs/㎡
Initial setting time: ≥2hours
Final setting time: ≤48hours
Construction temperature: +5℃~+35℃
Packaging: 17.2kgs/set
Implementation standard: GB/T23445-2009(II), specific indicators see technical parameters.
No | Project | Technical standard(II) | ||
1 | Setting time | Initial setting time/min ≥ | 45 | |
Final setting time/h ≤ | 24 | |||
2 | Impermeability pressure/Mpa | Coated specimen≥ | 7d | 0.5 |
Mortar specimen ≥ | 7d | 1 | ||
28d | 1.5 | |||
3 | Compressive strength/Mpa ≥ | 24 | ||
4 | Flexural strength/Mpa ≥ | 8 | ||
5 | Flexibility (transverse deformation capacity)/mm ≥ | 1 | ||
6 | Bond strength/Mpa ≥ | 7d | 1 | |
28d | 1.2 | |||
7 | Alkali resistance | No cracking, peeling | ||
8 | Heat resistance | No cracking, peeling | ||
9 | Frost resistance | No cracking, peeling | ||
10 | Shrinkage rate/% ≤ | 0.15 | ||
11 | Water absorption rate/% ≤ | 4 | ||
Transportation & storage
This product is non-flammable and explosive material, which can be transported according to general cargo. Sunscreen, freeze-proof, rain-proof, extrusion and collision should be avoided in transportation, and the packaging should be kept intact.
The product should be ventilated, dried and prevented from direct sunshine during storage. The storage temperature should be between 5 and 35℃.
Under normal storage and transportation conditions, the storage period is 12 months from the date of production.
Attention
After the waterproof layer is completely dry, the overburden construction can be carried out.
This material should be constructed in the environment of +5 - +35℃, and it is not suitable to be constructed outdoors in rainy weather.
This product is alkaline, if splashed into eyes will be irritating, should be washed with clear water in time.